Rare-earth magnet

src: upload.wikimedia.org

Rare-earth magnets are strong permanent magnets made from alloys of rare-earth elements (elements in the lanthanide series, plus scandium and yttrium). Developed in the 1970s and 1980s, rare-earth magnets are the strongest type of permanent magnets made, producing significantly stronger magnetic fields than other types such as ferrite or alnico magnets. The magnetic field typically produced by rare-earth magnets can exceed 1.4 teslas, whereas ferrite or ceramic magnets typically exhibit fields of 0.5 to 1 tesla. There are two types: neodymium magnets and samarium-cobalt magnets. Magnetostrictive rare-earth magnets such as Terfenol-D also have applications, e.g. in loudspeakers. Rare-earth magnets are extremely brittle and also vulnerable to corrosion, so they are usually plated or coated to protect them from breaking, chipping, or crumbling into powder.

The development of rare-earth magnets began around 1966, when K. J. Strnat and G. Hoffer of the US Air Force Materials Laboratory discovered that an alloy of yttrium and cobalt, YCo₅, had by far the largest magnetic anisotropy constant of any material then known. The term "rare earth" can be misleading, as these metals are not particularly rare or precious; they are about as abundant as tin or lead. However rare earth ores are unevenly distributed, with the major source being China, which has led countries to classify rare earth metals as strategically important. Recent Chinese export restrictions on these materials have led other countries to initiate research programs to develop strong magnets that do not require them.

Video Rare-earth magnet

Explanation of strength

The rare-earth (lanthanide) elements are metals that are ferromagnetic, meaning that like iron they can be magnetized to become permanent magnets, but their Curie temperatures are below room temperature, so in pure form their magnetism only appears at low temperatures. However, they form compounds with the transition metals such as iron, nickel, and cobalt, and some of these compounds have Curie temperatures well above room temperature. Rare-earth magnets are made from these compounds.

The greater strength of rare-earth magnets is mostly due to two factors. First, their crystalline structures have very high magnetic anisotropy. This means that a crystal of the material preferentially magnetizes along a specific crystal axis but is very difficult to magnetize in other directions. Like other magnets, rare-earth magnets are composed of microcrystalline grains, which are aligned in a powerful magnetic field during manufacture, so their magnetic axes all point in the same direction. The resistance of the crystal lattice to turning its direction of magnetization gives these compounds a very high magnetic coercivity (resistance to being demagnetized).

Second, atoms of rare-earth elements can have high magnetic moments because their orbital electron structure contains many unpaired electrons, in contrast to other elements, in which almost all of the electrons exist in pairs with opposite spins, so their magnetic fields cancel out. This is a consequence of incomplete filling of the f-shell, which can contain up to 7 unpaired electrons. In a magnet it is the unpaired electrons, aligned so they spin in the same direction, which generate the magnetic field. This gives the materials high remanence (saturation magnetization J_s). The maximal energy density BH_max is proportional to J_s², so these materials have the potential for storing large amounts of magnetic energy. The magnetic energy product BH_max of neodymium magnets is about 18 times greater than "ordinary" magnets by volume. This allows rare-earth magnets to be smaller than other magnets with the same field strength.

Maps Rare-earth magnet

Magnetic properties

Some important properties used to compare permanent magnets are: remanence (B_r), which measures the strength of the magnetic field; coercivity (H_ci), the material's resistance to becoming demagnetized; energy product (BH_max), the density of magnetic energy; and Curie temperature (T_C), the temperature at which the material loses its magnetism. Rare-earth magnets have higher remanence, much higher coercivity and energy product, but (for neodymium) lower Curie temperature than other types. The table below compares the magnetic performance of the two types of rare-earth magnets, neodymium (Nd₂Fe₁₄B) and samarium-cobalt (SmCo₅), with other types of permanent magnets.

Source:

src: www.strong-mag.com

Types

Samarium-cobalt

Samarium-cobalt magnets (chemical formula: SmCo₅), the first family of rare-earth magnets invented, are less used than neodymium magnets because of their higher cost and lower magnetic field strength. However, samarium-cobalt has a higher Curie temperature, creating a niche for these magnets in applications where high field strength is needed at high operating temperatures. They are highly resistant to oxidation, but sintered samarium-cobalt magnets are brittle and prone to chipping and cracking and may fracture when subjected to thermal shock.

Neodymium

Neodymium magnets, invented in the 1980s, are the strongest and most affordable type of rare-earth magnet. They are made of an alloy of neodymium, iron, and boron (Nd₂Fe₁₄B), sometimes abbreviated as NIB. Neodymium magnets are used in numerous applications requiring strong, compact permanent magnets, such as electric motors for cordless tools, hard disk drives, magnetic holddowns, and jewelry clasps. They have the highest magnetic field strength and have a higher coercivity (which makes them magnetically stable), but they have a lower Curie temperature and are more vulnerable to oxidation than samarium-cobalt magnets. Corrosion can cause unprotected magnets to spall off a surface layer or to crumble into a powder. Use of protective surface treatments such as gold, nickel, zinc, and tin plating and epoxy-resin coating can provide corrosion protection.

Originally, the high cost of these magnets limited their use to applications requiring compactness together with high field strength. Both the raw materials and the patent licenses were expensive. However, since the 1990s, NIB magnets have become steadily less expensive, and the low cost has inspired new uses such as magnetic construction toys.

src: www.umagnets.com

Hazards

The greater force exerted by rare-earth magnets creates hazards that are not seen with other types of magnet. Magnets larger than a few centimeters are strong enough to cause injuries to body parts pinched between two magnets or a magnet and a metal surface, even causing broken bones. Magnets allowed to get too near each other can strike each other with enough force to chip and shatter the brittle material, and the flying chips can cause injuries. There have even been cases where young children who have swallowed several magnets have had a fold of the digestive tract pinched between the magnets, causing injury and in one case intestinal perforations, sepsis and death.

The U.S. Consumer Product Safety Commission passed a rule restricting rare-earth magnet size in consumer products, but it was vacated by a US Federal court decision in November 2016.

src: cdn-shop.adafruit.com

Applications

Since their prices became competitive in the 1990s, neodymium magnets have been replacing Alnico and ferrite magnets in the many applications in modern technology requiring powerful magnets. Their greater strength allows smaller and lighter magnets to be used for a given application.

Common applications

Common applications of rare-earth magnets include:

• computer hard disk drives
• wind turbine generators
• audio speakers / headphones
• bicycle dynamos
• Magnetic resonance imaging devices
• fishing reel brakes
• permanent magnet motors in cordless tools
• high-performance AC servo motors
• traction motors and integrated starter-generators in hybrid and electric vehicles
• mechanically powered flashlights, employing rare earth magnets for generating electricity in a shaking motion or rotating (hand-crank-powered) motion
• industrial uses such as maintaining product purity, equipment protection, and quality control
• capture of fine metallic particles in lubricating oils (crankcases of internal combustion engines, also gearboxes and differentials), so as to keep said particles out of circulation, thereby rendering them unable to cause abrasive wear of moving machine parts

Other applications

Other applications of rare-earth magnets include:

• Linear motors (used in mag-lev trains, etc.)
• Stop motion animation: as tie-downs when the use of traditional screw and nut tie-downs is impractical.
• Diamagnetic levitation experimentation, the study of magnetic field dynamics and superconductor levitation.
• Electrodynamic bearings
• Launched roller coaster technology found on roller coaster and other thrill rides.
• LED Throwies, small LEDs attached to a button cell battery and a small rare earth magnet, used as a form of non-destructive graffiti and temporary public art.
• Neodymium magnet toys
• Electric guitar pickups
• Miniature figures, for which rare-earth magnets have gained popularity in the miniatures gaming community for their small size and relative strength assisting in basing and swapping weapons between models.

src: images-na.ssl-images-amazon.com

Rare-earth-free permanent magnets

The United States Department of Energy has identified a need to find substitutes for rare-earth metals in permanent-magnet technology and has begun funding such research. The Advanced Research Projects Agency-Energy (ARPA-E) has sponsored a Rare Earth Alternatives in Critical Technologies (REACT) program, to develop alternative materials. In 2011, ARPA-E awarded 31.6 million dollars to fund Rare-Earth Substitute projects.

src: s-media-cache-ak0.pinimg.com

References

src: www.qiannipicture.com

Further reading

• Edward P. Furlani, "Permanent Magnet and Electromechanical Devices: Materials, Analysis and Applications", Academic Press Series in Electromagnetism (2001). ISBN 0-12-269951-3.
• Peter Campbell, "Permanent Magnet Materials and their Application" (Cambridge Studies in Magnetism)(1996). ISBN 978-0-521-56688-9.
• Brown, D. N.; B. Smith; B. M. Ma; P. Campbell (2004). "The Dependence of Magnetic Properties and Hot Workability of Rare Earth-Iron-Boride Magnets Upon Composition" (PDF). IEEE Transactions on Magnetics. 40 (4): 2895-2897. Bibcode:2004ITM....40.2895B. doi:10.1109/TMAG.2004.832240. ISSN 0018-9464. Archived from the original (PDF) on 2012-04-25. 

src: images.homedepot-static.com

External links

• Standard Specifications for Permanent Magnet Materials (Magnetic Materials Producers Association)
• Edwards, Lin (22 March 2010). "Iron-nitrogen compound forms strongest magnet known". PhysOrg. 

Source of the article : Wikipedia